H06-2 Epoxy Ester Iron Red Primer


Adding iron oxide red and zinc yellow pigment after epoxy resin and seed fat alcoholized, adding dimethyl benzene and butyl alcohol after rubbing with body pigment.


Suitable to coating black metal, especially as primer for surface of metal in costal areas and wet and torrid zone.


Hard film, good adhesion, increasing resistance to wet pick and salt fog when used with etching primer.

Physical Parameter:

Specific Gravity: 1.32kg/L 

Color: Iron red

Theoretic Dosage: 0.16 kg/m2

Film Thickness: WFT: 100μm    DFT:  40μm 

Drying Time: 23±2℃,  Dust-Free: ≤2 h,  Non-dint Drying ≤18 h

Storage: 1 year

Flash Point: 30℃

Application Parameter:

Formula Ratio: One pot

Curing Time:  Use directly after being opened 

Pot Life:  Infinite

Coating Method:  High-pressure airless spray, hand brushing, roll coating

Diluent/ Dilution Ratio: Diluent for F102 epoxy coatings,     <5%

Coating Interval:  25℃, Min. 24 h,   Max.  Infinite

Surface Treatment: Sand blasting must be made on surface of new steel till qualified to Sa2.5, If needing to protect steel temporarily, appropriate shop primer should be used. Do clean the wear shop primer and dirt before painting.

Recommended Layers:  2 layers of high-pressure airless spray, 80μm DFT

Post-Coat Accessory Coatings: Alkyd coatings and phenolic resin coatings.


The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coating itself if it is used in other sectors undescribed herein or fresh sectors.