Component:

Antirust pigment of epoxy ester resin, zinc yellow and zinc oxide, filler, dryer, antirust additives, mixed solvent, etc.

Application:

Suitable for surface of light metal, especially used as antirust primer for the littoral and damp and hot areas

Properties:

Air-drying or low temperature baking, tough and wearing film, good adhesion, increasing properties of damp proofing and salt fog proofing by using with phosphating primer.

Physical Parameter:

Color: Zinc yellow

Specific Gravity: Approx. 1.32 kg/L 

Theoretic Dosage: 0.16 kg/m2

Film Thickness: WFT: 90μm DFT: 40μm

Drying Time: Dust-Free: ≤2 h, Non-dint Drying: ≤18 h

Flash Point: 30 ℃

Storage: 1 year

Application Parameter:

Formula Ratio: One pot

Curing Time: Use directly after being opened

Pot Life: Infinite

Coating Method: High-pressure airless spray, Hand brushing, roll coating

Diluent/ Dilution Ratio: Diluent for 102 epoxy coatings, <5%

Coating Interval: 25℃, Min. 24; Max. Infinite

Surface Treatment: Sand blasting must be made on surface of steel till qualified to Sa 2.5. Generally, controlling the crudity on surface of steel between 40~80μm or 1/3~1/1.25 of the total coating, coating within 24 h after antirusting.

Recommended Layers: 2 layers of high-pressure airless spray, 80μm DFT, 

Pre-Coat Accessory Coatings: X06-1 Ethene phosphating primer

Post-Coat Accessory Coatings: Alkyd resin coatings and phenolic resin coatings, etc.

Claim:

The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coating itself if it is used in other sectors undescribed herein or fresh sectors.