H53-85 Epoxy MIO Sealing Paint

Component:

Two-component (A and B) coatings made from epoxy resin, MIO, antirust paint, screening agent, solvent, additives and curing agent.


Application:

Anti-corrosion primer, semi-paint for anticorrosion coating, increasing the properties of sealing and anticorrosion used with epoxy zinc rich primer.


Properties:

Excellent properties of sealing and adhesion on zinc rich primer and zinc coating, hard film, resistance to wear, keeping impact resistance and elasticity for a long-term, good durability, good ply adhesion with post paint.


Physical Parameter:

Color: Grey 

Density: 1.37 kg/L 

Film Thickness: WFT: 200μm DFT: 100μm

Theoretic Dosage: 0.27 kg/m2

Flash Point: Component A (Binder) 27℃; Component B (Curing Agent) 27℃

Drying Time: 23℃, Dust-Free: ≤4 h, Hard Drying: ≤48 h, Fully Curing: 7d

Storage: 1 year


Application Parameter:

Formula Ratio: Component A : Component B = 10 : 1 (Weight Ratio)

Curing Time: 23℃, 30 min

Pot Life: 23℃, 8 h, unsuitable for application below 5℃

Coating Method: Spraying, hand brushing, roll coating

Diluent/ Dilution Ratio: Diluent for F102 epoxy resin coatings, <5%

Surface Treatment: Sand blasting must be made on surface of steel till qualified to Sa 2.5 or hand rust removing till qualified to St 3.

Pre-Coat Accessory Coatings: Zinc rich primer and epoxy iron red antirust paint, etc.

Post-Coat Accessory Coatings: Top coat of epoxy, epoxy asphalt, chlorinated rubber, polyurethane and acrylic acid, etc.

Coating Interval: 23℃, Min. 6 h, Max. 30 h


Claim:

The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coating itself if it is used in other sectors undescribed herein or fresh sectors.