Component:
Using chlorinated rubber as binder, adding synthetic resin, platicizer, pigment, additive, solvent, etc.

Application:
Anticorrosive topcoat of bridge, tower, port establishment, sea building, ektexine of gas burner, places eroded by salt and base, and all steel structures eroded by chemical gas.

Properties:
Good tenacity of film, excellent resistance to water, weather, chemicals and exposure.

Physical Parameter:
Color: All colors

Specific Gravity: Approx. 1.2 kg/L

Film Thickness: WFT: 105μm    DFT:  40μm

Theoretic Dosage: 0.16 kg/m2

Flash Point: 38℃

Drying Time: 23℃,  Dust-Free: ≤0.5 h,  Hard Drying: ≤6 h

Storage: 1 year

Application Parameter:
Formula Ratio: One pot

Curing Time: Instant usage after blending

Pot Life: No limits

Coating Method: High-Pressure airless spray, hand brushing, roll coating

Diluent/Dilution Ratio: 101 chlorinated rubber coatings diluent, <5%

Surface Treatment: If the pre-paint is stained, the grease and dust should be removed.

Recommended Layers: 2 layers (high-pressure airless spray), 80~90μm DFT

Coating Interval: 23℃: Min. 6 h,  Max. Infinite

Pre-Coat Accessory Coatings: J52-84 chlorinated aluminum flake mastic antirust paint, J52-64 chlorinated MIO antirust paint, J53-16 chlorinated antirust paint, H53-6 epoxy MIO antirust paint, H53-85 epoxy MIO seal coat.

Claim:
The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coatings itself if it is used in other sectors undescribed herein or fresh sectors.