Component:
Chlorinated rubber, asphalt, antirust pigment, filler, additive, solvent, etc. Two containers (A and B).

Application:
Corrosion prevention of bottom of ships, ballast tank, steel strobe, underwater facilities and mine derrick. Intermediate layer of epoxy asphalt coatings and chlorinated rubber topcoat. Refinish paint of epoxy asphalt coatings.

Illumination:
Excellent Resistance to damp, rust, and humidity-dry cycling, good adhesion and drying property, suitable for construction under low temperature in winter.

Physical Parameter:
Color: Brown black

Specific Gravity: Approx. 1.25 kg/L

Theoretic Dosage: 0.19 kg/m2

Flash Point: 25℃, component A: 50℃, component B: 33℃

Film Thickness: WFT: 120μm    DFT:  50μm

Storage:  1 year

Drying Time: 25℃,  Dust-Free: ≤2 h,  Hard Drying: ≤12 h

Application Parameter:

Formula Ratio: Component A：Component B=1：1

Curing Time: Instant usage after blending

Pot Life: No limits

Coating Method: High-pressure airless spray, hand brushing, roll coating

Diluent/Dilution Ratio: 101 chlorinated rubber coatings diluent, <5%

Coating Interval: 0℃: Min. 24h; Max. Infinite; 20℃: Min. 8h; Max. Infinite; 30℃: Min. 6h, Max. Infinite

Surface Treatment: Sand blasting must be made on surface of steel if coated directly on steel till qualified to Sa 2.5 Standard of Sweden. Secondary derusting must be made on the shop primer coated surface till qualified to St 3 Standard of Sweden.

Pre-Coat Accessory Coatings: Zinc rich paint, X06-1 vinyl etching primer, H52-61 epoxy asphalt mastic coatings, coated directly on derusted steel.

Post-Coat Accessory Coatings: Chlorinated rubber mastic topcoat

Claim:
The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coatings itself if it is used in other sectors undescribed herein or fresh sectors.