Component:

Chlorinated rubber, plasticizer, micaceous iron oxide (MIO), additive, solvent, etc.

Application:

Corrosion protection of ships, gas jar, marine project, petrochemical equipment and other steel structures, as well as protection layer of concrete.

Properties:

MIO is a scaly pigment, which has unique barrier property and pigment percentage can range directionally parallel and overlapping to form scale-like structure, so this film has excellent resistance to rust, humidity and chemicals.

Physical Parameter:

Color: Dusty black or maroon

Specific Gravity: Approx. 1.50 kg/L

Theoretic Dosage: 0.16kg/m2

Storage: 1 year

Film Thickness: WFT: 125μm DFT: 40μm

Flash Point: 31℃

Drying Time: 25 ℃, Dust-Free: ≤2 h, Hard Drying: ≤8 h

Application Parameter:

Formula Ratio: One pot

Curing Time: Instant usage

Pot Life: No limits

Coating Method: High-pressure airless spray, hand brushing, roll coating

Diluent/Dilution Ratio: 101 chlorinated rubber coatings diluent, <5%

Coating Interval: 0℃: Min. 24h; Max. Infinite; 20℃: Min. 8h; Max. Infinite; 30℃: Min. 6h, Max. Infinite

Surface Treatment: Secondary derusting must be made on the shop primer coated surface till qualified to St 2.5 Standard of Sweden. If the chlorinated rubber aluminum anticorrosion paint coated surface has been exposed in polluting environment for a long time, it should be washed by high pressure freshwater and dried before coating.

Recommended Layers: 2 layers, 70~100μm DFT

Pre-Coat Accessory Coatings: H06 epoxy zinc rich shop primer, H06-1 epoxy zinc primer, H53-5 epoxy iron red shop primer, E06 inorganic zinc shop primer, E06-28 inorganic zinc silicate primer, J52-84 chlorinated rubber aluminum flake derusting paint, etc.

Post-Coat Accessory Coatings: Chlorinated rubber topcoat, acrylic topcoat, etc.

Claim:

The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coatings itself if it is used in other sectors undescribed herein or fresh sectors.