Component:

Chlorinated rubber, plasticity agent, antirust pigment and solvent, etc.

Application:

Anticorrosion primer for bridge, tower, port machine, structures on sea, chemical equipments, exterior on gas cabinet, and all metal structures corrupted by chemical air.

Properties:

Hard film, excellent water proofing , resistance to alkali, salt fog resistance, humid-dry cycling resistance, resistance to cathodic protection zeta-potential, quick drying, good interlayer adhesion, and excellent antirust property.

Physical Parameter:

Color: Iron red

Density: 1.27 kg/L

Film Thickness: WFT: 126μm DFT: 40μm

Theoretic Dosage: 0.16 kg/m2

Flash Point: 38℃ 

Drying Time: 23℃, Dust-Free: ≤2 h, Hard Drying: ≤12 h

Storage: 1 year

Application Parameter:

Formula Ratio: One pot

Curing Time: Use after being opened and fully stirred

Pot Life: Infinite

Coating Method: High-pressure airless spray, hand brushing, roll coating

Diluent/ Dilution Ratio: Diluent for 101 chlorinated rubber coatings, <5%

Surface Treatment: Sand blasting must be made on surface till qualified to Sa 2.5 or hand rust removing till qualified to St3. Secondary rust removing must be made on surface of shop primer till qualified to St3 

Pre-Coat Accessory Coatings: Coating on surface of steel rust removing qualified to Sa2.5 directly, suitable for using with shop primer of inorganic zinc and epoxy zinc rich and chlorinated rubber aluminum antirust paint.

Post-Coat Accessory Coatings: J53-61 chlorinated rubber MIO antirust paint, J52-63 chlorinated rubber topcoat

Coating Interval: 23℃, Min. 6 h, Max. Infinite

Claim:

The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coating itself if it is used in other sectors undescribed herein or fresh sectors.