Component:
Perchlorinated polyethylene, synthetic resin, plasticizer, iron oxide red, additive, solvent, etc.

Application:
Surface corrosion protection of various steel structures or concrete eroded by chemical gas, industrial gas and acid, base and salt.

Properties:
Excellent corrosion prevention, resistance to salt fog, humidity-dry cycling, film flexibility, adhesion, fast drying, and applicable in low temperature.

Physical Parameter:
Color: Iron red

Specific Gravity: Approx. 1.30 kg/L

Drying Time: 25℃,  Dust-Free: ≤1 h,  Hard Drying: ≤24 h

Theoretic Dosage: 0.17 kg/m2

Flash Point: 26℃

Storage:  1 year

Film Thickness: WFT: 135μm    DFT:  45μm

Application Parameter:
Formula Ratio: One pot

Curing Time: Instant usage

Pot Life: No limits

Coating Method: High-Pressure airless spray, hand brushing, roll coating

Diluent/Dilution Ratio: 109 perchlorinated polyethylene coatings diluent, <5%

Coating Interval: 0℃:Min. 24 h, Max 7 d; 20℃: Min. 8 h, Max. 7 d; 30℃: Min. 6 h,  Max. 7 d

Surface Treatment: Impact cleaning or sand blasting of steel surface till qualified Sa 2.5, or hand cleaning and kinetic machine de-rusting till to St 3 Standard of Sweden.

Recommended Layers: 2 layers (spray or hand brushing), 80~90μm  DFT

Pre-Coat Accessory Coatings: H06 epoxy zinc rich shop primer, H06-1 epoxy zinc primer, H53-5 epoxy iron red shop primer, E06 inorganic zinc shop primer, E06-28 inorganic zinc silicate primer

Post-Coat Accessory Coatings: X53-4 perchlorinated polyethylene MIO anticorrosion paint, X52-11 perchlorinated polyethylene enamel (outdoor), X52-12 perchlorinated polyethylene enamel (indoor).

Claim:
The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coatings itself if it is used in other sectors undescribed herein or fresh sectors.