Component:

Chlorosulphonated polythylene rubber as binder, modified resin, pigment filler, additives, curing agent and solvent, etc. Two-component (A and B) package for this coatings.

Application:

Sign and protection for concrete chimney and conveying electricity pole, etc.

Illumination:

Excellent resistance to ageing of weather, acid, base and salt, good resistance to water, heat, cold, and hydronium irradiation, quick dying, suitable for construction in low temperature, good penetrability, color coating and good color and gloss retention.

Properties:

Color: White or bright red

Specific Gravity: Approx. 0.96 kg/L

Theoretic Dosage: 0.2 kg/m2

Flash Point: Component A, 20℃; Component B, 10℃

Storage: Component A, 8 Months; Component B, 6 Months

Drying Time: 25℃, Dust-Free: ≤0.5 h, Hard Drying: ≤24 h, Fully Curing: 7 d

Film Thickness: WFD: 160μm;   DFT: 25μm

Physical Parameter:

Formula Ratio: Component A : Component B = 10 : 1

Curing Time: Use directly after mixing

Pot Life: 25℃, 12 h

Coating Method: High-pressure airless spray, hand brushing, roll coating

Diluent/ Dilution Ratio: Diluent only for 102 chlorosulphonated polythylene coatings,     <5%

Coating Interval: 25℃, Min. 0.5 h,  Max. 7d

Surface Treatment:  (1) concrete surface must be flat and no mineral particle, flexible oil, oil besmirch and adhesive objects, sealer must be used if the surface is unflat.

                 (2) coating after new concrete surface reaching the demand of standard maintenance strength; 

                 (3) dry concrete surface, water content ≤6%

Recommended Layers: 4 layers, 100μm DFT.

Claim:

The data in this Specification is derived from experiments and practical applications, and can be regarded as a guide for application. The title product is only for specialty application. Otherwise we only guarantee the quality of the said coating itself if it is used in other sectors undescribed herein or fresh sectors.